Copper Alloys

  COPPERS HIGH PERFORMANCE ALLOYS BRASSES LEADED BRASSES TIN BRASSES
OLIN Alloy No. 102 110 122 1093 151 194 195 197 210 220 226 230 240 260 268 350 353 405 411 422 425
ASTM Spec. No. B152 B152 B152 B152 B747 B465 B465 B465 B36 B36   B36 B36 B36 B36 B121 B121 B591 B591 B591 B591
Density 0.323 0.322 0.323 0.322 0.323 0.322 0.322 0.319 0.32 0.318 0.317 0.316 0.313 0.308 0.306 0.306 0.306 0.319 0.318 0.318 0.317
Mod. of Elast. 17 17 17 17 17 17 17 17 17 17 17 17 16 16 15 15 15 16 16 16 16
Elect. Cond. 101 101 85 101 95 60 50 80 56 44 40 37 32 28 27 26 26 41 32 31 28
Therm. Cond. 226 226 196 226 208 150 115 185 135 109 100 92 81 70 67 67 67 95 75 75 69
Coef. of Th. Exp. 9.8 9.8 9.8 9.8 9.8 9.7 9.6 9.6 10 10.2 10.3 10.4 10.6 11.1 11.3 11.3 11.3 10.2 10.2 10.2 10.2
TENSILE STRENGTH x 1000 PSI (Kgf/mm2 = KSI x .7031)
YIELD STRENGTH x 1000 PSI (Nominal 0.2% offset) (Kgf/mm2 = KSI x .7031)
ANNEALED 26-38 37-42 40-63 50-60 43-53 34-40 36-42 37-45 39-47 44-54 45-61 44-61 47-59 46-54 38-45 38-44 41-49 41-47
10 13 38 28 23 10 12 15 13 20 21 23 23 21 16 14 19 17
1/4 HARD 34-42 40-45   60-72   37-47 40-50 42-52 44-54 48-58 49-59 49-59 49-59 49-59 41-53 42-54 47-57 49-59
32 35   57   30 33 32 35 29 33 34 32 29 38 35 38 37
1/2 HARD 37-46 43-51 53-63 68-78 53-63 42-52 47-57 49-59 51-61 55-65 57-67 55-65 55-65 55-65 46-58 49-60 54-65 57-69
37 42 45 71 48 44 47 50 48 42 51 44 46 42 43 49 55 58
3/4 HARD 41-50 47-56   75-85   46-56 52-62 55-65 57-67 61-71 64-74 62-72 62-72 62-72 52-64 55-66 60-72 62-74
43 50   77   50 54 58 55 53 62 53 60 55 55 58 64 64
HARD 43-52 53-62 60-70 82-90 60-70 50-59 57-66 60-69 63-72 68-77 71-81 68-78 68-78 68-78 58-70 61-72 67-79 70-82
45 56 60 83 60 53 58 62 61 61 72 57 68 67 63 64 71 72
EX. HD. 47-56 59-65 67-73   67-73 56-64 64-72 69-77 72-80 78-87 83-92 79-89 79-89 79-89 63-75 67-78 75-85 76-88
50 60 67   67 59 63 70 68 68 83 67 79 78 68 70 75 79
SPRING 50-58 64-71 70-76 88-97 70-76 60-68 69-77 75-83 78-86 85-93 91-100 86-95 86-95 86-95 68-80 73-83 82-92 84-94
52 66 70 88 70 63 68 76 72 76 86 71 84 84 73 75 82 90
EX. SPR. 52 Min   73-80   70-78 61-69 72-80 78-86 82-90 89-97 95-104 90-99 90-99 90-99 73-84 78 Min 88 Min. 92 Min
51 Min   73   74 64 70 78 76 78 89 73 89 88 77 75 Min 82 Min 87 Min
ELONGATION Nominal % in 2 inches (= % in 50mm)
ROCKWELL B HARDNESS Nominal-.020′ gauge and over (Rockwell F, 30T, or 15N where noted)
ANNEALED 35 38 23 26 20 Min. 45 47 40 45 50 53 52 50 56 45 43 45 48
  49F       45F 65F 64F 71F 70F 75F 75F 80F 72F 61F 68F 72F 72F
1/4 HARD 23 22   14   30 27 28 27 26 46 42 44 48 34 23 29 35
72F 32   71   36 41 44 47 51 52 52 52 52 46 47 56 59
1/2 HARD 20 15 17 6 17 17 12 19 14 18 30 36 28 35 27 13 16 20
83F 37 59 78 66 50 58 61 63 66 68 65 65 65 59 61 70 70
3/4 HARD 14 8   3   9 6 9 8 10 16 25 16 21 17 7 7 15
86F 47   81   57 64 68 71 74 77 75 75 75 67 69 76 79
HARD 9 4 7 2 7 5 4 6 7 4 10 19 9 12 10 6 4 9
89F 57 71 83 69 62 70 73 76 80 82 80 80 80 72 74 80 85
EX. HD. 4 2 2   6 2 Max 2 4 4 2 3 7 4 6 7 4 2 6
91F 60 74   72 68 75 78 81 86 88 86 86 86 75 79 83 90
SPRING 3 1 Min 2 2 5 2 Max 1 Min 3 3 1 Min 1 Min 5 3 4 5 3 2 4
94F 62 Min 76 85 74 71 78 81 84 89 91 89 89 89 79 82 86 92
EX. SPR. 3 Max   2 Max   1 Min. 2 Max 1 Max 3 Max 2 Min 1 Max 1 Min 5 Max 1 Min 5 Max 4 Max 2 Max 2 Max. 2 Max
92 MinF   77   75 72 80 83 86 90 93 90 90 90 81 80 Min 86 Min 92 Min

 

  PHOSPHOR BRONZES HIGH PERFORMANCE ALLOYS CUPRO-NICKELS Cu-Ni-Sn NICKEL SILVERS BERYLLIUM COPPERS
OLIN Alloy No. 505 510 511 521 544 638 654 664 688 7025 706 715 725 752 762 770 17510 170 172
ASTM Spec. No. B508 B103 B103 B103 B103 B422 B96 B694 B592 B422 B122 B122 B122 B122 B122 B122 B534 B194 B194
Density 0.321 0.32 0.32 0.318 0.321 0.299 0.309 0.317 0.296 0.318 0.323 0.323 0.321 0.316 0.31 0.314 0.319 0.304 0.302
Mod. of Elast. 17 16 16 16 15 17 17 16 17 19 18 22 20 18 18 18 20 19 19
Elect. Cond. 48 15 20 13 19 10 7 30 18 40 9 4.6 11 6 9 5.5 45 20 20
Therm. Cond. 120 40 48.4 36 50 22 21 67 47 98 26 17 31 19 24 17 100 45 45
Coef. of Th. Exp. 9.9 9.9 9.9 10.1 9.6 9.5 9.7 9.7 10.1 9.8 9.5 9 9.2 9 9 9.3 9.8 9.7 9.7
TENSILE STRENGTH x 1000 PSI (Kgf/mm2 = KSI x .7031)
YIELD STRENGTH x 1000 PSI (Nominal 0.2% offset or range) (Kgf/mm2 = KSI x .7031)
ANNEALED 38-42 46-56 46-54 56-65 45-52 77-87 75-90 58-68 77-87 90-110 43-50 52 Min 45-65 53-63 57-75 61-76 100-130 100 Min 100 Min
(TM00 / AM) 13 24 22 29 21 56   44 52 65-90 19 28 21 25 36 32 80-110 70-95 70-95
1/4 HARD 41-51 49-61 46-58 63-75 47-59 90-102 75-90 67-77 87-101   51-67 58-72 55-75 58-72 65-81 69-87   110 Min 110 Min
(TM01 / 1/4 HM) 30 37 35 48 38 82 60 65 76   53 47 73 Max 45 52 63   80-110 80-110
1/2 HARD 48-58 58-73 55-70 69-84 55-70 100-112 86-101 74-84 97-112 95-120 58-72 66-80 65-80 66-80 75-91 78-95   120 Min 120 Min
(TM02 / 1/2 HM) 47 57 56 63 57 93 79 76 92 85-110 63 68 68 63 70 78   95-125 95-115
3/4 HARD 54-64 68-79 67-82 80-92 63-74 105-117 97-112 79-89   100-125       74-86 83-98 88-101      
(TM03) 57 68 72 77 66 99 92 81   95-120       75 82 92      
HARD 59-69 76-91 72-87 85-100 72-87 114-126 108-120 83-93 106-120   71-83 75-88 75-90 78-91 90-105 92-107 110-140 135 Min 135 Min
(TM04 / HM) 62 81 76 86 77 108 101 85 101   75 78 80 82 89 98 100-130 110-135 110-135
EX. HD. 65-75 88-103 84-99 97-112 84-99 118-130 116-126 89-99 113-127   73-85 80-92 80-95 86-98 101-114 102-115   150 Min 150 Min
(TM05 / SHM) 68 93 88 99 88 112 109 89 108   76 83 85 91 98 107   125-145 125-145
SPRING 70-79 95-110 91-105 105-119 91-105 123-134 124-133 92-102 123-133   78-88 84-94 85-100 90-101 109-122 108-120 120-150 160 Min 160 Min
(TM06 / XHM) 72 100 94 106 88 Min 116 117 92 114   76 Min 86 90 93 105 112 110-140 135-160 135-170
EX. SPR. 75-84 100-114 96-109 110-122 96-109 130 Min 131-140 95-105 125 Min       90-105 96 Min 114 Min 116 Min   — 175 Min
(TM08 / XHMS) 77 104 98 110 88 Min 119 Min 124 93 112 Min       95 95 Min 102 Min 115 Min   — 150-175
ELONGATION Nominal % in 2 inches (= % in 50mm)
ROCKWELL B HARDNESS Nominal-.020″ gauge and over (Rockwell F, 30T, 15N or Hv where noted)
ANNEALED 44 55 47 63 46 33   24 35 10 Min 35 30 Min 35 35 40 43 10 Min 18 Min 18 Min
(TM00 / AM) 69F 78F 75F 86F 71F 74 (30T)   97F 68 (30T) — 75F 83F 50Max30T 85F 90F 87F 195-235H 220-260H 220-260H
1/4 HARD 33 41 36 50 33 16 33 13 19   12 17 5 Min 24 35 26   15 Min 16 Min
(TM01 / 1/4 HM) 48 60 46 74 46 94 81 79 90   64 74 85 Max 62 73 75   240-280H 240-280H
1/2 HARD 17 24 21 37 19 10 23 7 9 7 Min 5 6 10 14 18 14   12 Min 14 Min
(TM02 / 1/2 HM) 56 72 67 80 67 96 92 86 95 — 73 80 80 75 84 86   260-310H 260-310H
3/4 HARD 9 15 10 25 11 7 13 5   5 Min       8 10 8      
(TM03) 68 82 78 89 77 98 95 85   —       81 88 90      
HARD 5 10 7 21 6 4 6 4 4   1 Min 3 3 5 4 4 8 Min 9 Min 11 Min
(TM04 / HM) 73 88 85 93 85 99 97 87 97   81 86 82 85 92 93 220-290H 300-350H 300-350H
EX. HD. 3 4 3 13 3 3 4 4 2   1 Min 2 2 3 2 1 Min   9 Min 10 Min
(TM05 / SHM) 77 92 90 96 90 100 98 90 98   84 88 87 90 96 97      
SPRING 2 Min 2 Min 3 6 4 Max 2 3 3 1 Min   1 Max 1 Min 1 Min 1 Min 1 Max 1 Max 1 Min 4 Min 5 Min
(TM06 / XHM) 81 95 92 98 92 100 100 90 99   87 89 90 92 98 98 220-290H    
EX. SPR. 1 Min 2 2 4 4 Max 2 Max 2 3 2 Max       1 Max 2 Max 1 Max 1 Max   — 3 Min
(TM08 / XHMS) 83 96 93 99 93 100 Min 101 91 99 Min       91 92 Min 98 Min 98 Min   —